Irradiation Cross-Linked LSZH Flame Retardant Oil Resistant Po/Poe Polyolefin Pellet for Cable Jacket Compound

• Application: Communication
• Type: as Customized
• Connection Structure: as Customized
• Material Shape: Granuel
• Allowed Lateral Pressure: as Customized
• Allowed Tensile Strength: as Customized
• Model NO.: T-PO23
• Core: as Customized
• Certification: CE, ISO9001
• Brand: as Customized
• Sheath Material: Polyolefin
• Transport Package: Standard
• Specification: 9002-88-4
• Origin: China

Product Description

T-PO(23)  Series 
Irradiation cross-linked,low-smoke,halogen free and flame retardant polyolefin jacket compound,based on special POE resin,is produced by special technology with adding modifier,flame retardant and other special additives.

Type and application

Type		Product					Application
T-PO023F-5105		105ºC irradiation cross-linked,low-smoke,halogen free and flame retardant polyolefin jacket compound					For wire and car wire
T-PO023F-5125		125ºC irradiation cross-linked,low-smoke,halogen free and flame retardant polyolefin jacket compound					For wire and car wire
T-PO023F-5125NY		125ºC irradiation cross-linked,low-smoke,halogen free,flame retardant and oil resistant polyolefin jacket compound					For wire and car wire
T-PO023F-5150		150ºC irradiation cross-linked,low-smoke,halogen free and flame retardant polyolefin jacket compound					For wire and car wire

Processing
The following temperature profile of extruder is recommended:

Zone			Zone1	Zone2	Zone3	Zone4	Zone5	Head	Die
ºC Temperature	T-PO023F 5105		120	130	140	150	155	160	160
	T-PO023F 5125		120	130	140	150	155	160	160

Properties

Item		Unit	Typical value
			T-PO023F-5105	T-PO023F-5125		T-PO023F 5125NY	T-PO023F-5150
Specific gravity		g/cm³	1.45	1.46		1.46	1.48
Service temperature		ºC	105	125		125	150
Tensile strength at break		MPa	12.5	12.3		13.2	12.2
Elongation at break		%	190	195		220	200
Thermal Elongation (200ºC, 15Min,0.2MPa)	Elongation under      load	%	56	58		62	40
	Permanent   deformation after cooling	%	3	5		3	2
Air oven-7days (168hrs.) At 158ºC	Tensile     changed	%	-6*	-13		-6	9△
	Elongation     changed	%	-8*	-9		-9	-11△
Ol		%	35	36		35	36
Smoke Density	Non-flame	%	185	184		174	150
	Flame	%	65	70		70	60
Acid gas contained		mg/g	0.03	0.02		0.01	0.01
PH value			5.6	5.7		5.6	5.8
Electrical Conductivity		μS/mm	1.7	1.9		1.6	2.1
Toxicity Index			1.4	1.5		1.3	1.4

Note: The aging condition with * is 136 ºC, 168 hours; The aging condition with △ is 180 ºC for 168 hours.

Packaging Storage And Transport
Damp-proof packing was used for every 25kg/bag.The storage place should be in clean,cool,dry and ventilated conditions.Compound should be dried at 75ºC before use,which has keep in storage for a long time.

What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products