Customization: | Available |
---|---|
CAS No.: | 9002-86-2 |
Formula: | C2h3cl |
Still deciding? Get samples of $ !
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment Methods: |
![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() ![]() |
---|---|
Support payments in USD |
Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Physical Property
No. | Inspection items | Standard request | Test method | Typical value | |
Technical Index | |||||
1 | Density g/cm3 | / | GB 1033 | 1.45 | |
2 | Tensile strength MPa | ≥15 | GB 1040 | 18 | |
3 | Elongation at Break % | ≥180 | GB 1040 | 250 | |
4 | Hot deformation rate (90ºC×4h) % | ≤50 | GB8815 | 20 | |
5 | Brittle temperature Test temperature-25ºC |
Failed No.≤15/30 | GB5470 | Pass | |
6 | 200 ºC static thermal stability min | ≥60 | GB8815 | 65 | |
7 | Volume Resistivity at 20ºC Ω .m | ≥1× 1011 | GB/T 1410 | 3 × 1011 | |
8 | Dielectric Strength MV/m | ≥20 | GB/T1408. 1 | 21 | |
9 |
Thermal aging property | 100±2ºC , 168h | |||
Tensile strength MPa | ≥15 | GB1040 |
Pass | ||
Max Variation on Tensile Strength % | ±20 | ||||
Elongation at break % | ≥180 | ||||
Max Variation on Elongation at break % | ±20 | ||||
10 | Thermal aging quality loss | ºC | 100±2 | GB/T2951 | |
h | 168 |
Quality loss g/m2 | ≤20 | 8 | |||
Quality of Appearance | |||||
1 | Appearance | Extruded lines are smooth |
Eye survey | ||
2 |
Color | Consistent color tone | Eye survey | ||
Standard deviation ≤1.5 | Colorimeter | ||||
*Note: 1 The extruded lines are smooth, and no more than 3 floating points with a diameter ≥1.0mm are allowed within 1 meter.No particles ≥ 3.0mm are allowed. 2 All products shall undergo initial inspection upon startup, including appearance, color, density, etc. 3 If the first sample test fails, a retest is required, and the result of the second test is the judgment standard. |
Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Zone 5 | Zone 6 | Zone 7 | Head | Die |
TemperatureºC | 140 | 150 | 155 | 165 | 165 | 170 | 170 | 175 | 175 |
1.What Kind of Company Are We?
Shanghai Gengyun Industrial Co., Ltd., based on the development of technology forum OF telecom optical&electric cable equipment and materials(TOEM), is mainly engaged in investment, trade, and technical services in the field of telecom optical & electric cable.
We provide our customers with complete materials demand solutions, as well as overall solutions and customized services in factory design, equipment configuration, product development and raw material supply.
2.Why Choose Our Company?
Our company was established in 2008 and has 16 years of experience in the communications industry. We can provide professional optoelectronic cable solutions and support product customization. Our products and raw materials are 100% in line with industry standards. We have warehouses all over the country. Such as Shanghai, Jiangsu, Qingdao, Beijing and so on.
3.Are Samples Free?
For most raw materials,optical fiber and optical cables, we can provide free samples. For cable manufacturing equipment, we can provide factory test reports of various indicators.
4.Is the Product Variety Rich?
We have quite a wide variety of products.
Our products contain raw materials for optical fiber & cable, telecommunication cable include PE, PVC, FRP, PBT, water blocking yarn, water blocking tape, optical fiber ink, optical fiber, steel plastic composite tape, aluminum plastic composite tape, aramid yarn, etc. and
equipment for cable manufacturing including high-speed fiber coloring and rewinding machine, fiber merging machine, fiber screening and rewinding machine, special fiber drawing machine, coating production line, high-speed cable forming production line. There are different models of products under each category, and customization is supported.