LSZH Low Smoke Zero Halogen Flame Retardant Virgin Recycled Polyolefin Compound for Fiber Cable Sheath

• CAS No.: 9002-88-4
• Formula: (C2h4)N
• Material: Polyolefin
• Usage: General Plastics, Engineering Plastics, Specialty Plastics, Flame Retardant Wires and Cables
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Model NO.: T-PO001
• Color: White Black with Color Masterbatch If Needed
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Origin: China

Product Description

 Colour: White,Black(With Color Masterbatch If You Need Other Colour) 

70ºC Thermoplastic Low-Smoke Zero-Halogen Flame Retardant Polyolefin Compound
1.Type And Application
Type		Product name				Application
T-PO001		70°ºC Thermoplastic low-smoke z ero-halogen and flame retardant Polyolefin compounds				90%pass the single buming cable meet the requirements of high-speed extrusion process,compliance with ROHS,applicable to covered wire cable(Meet 50%light transmittance)
2.Product Description
Thermoplastic low-smoke zero-halogen  and  flame retardant polyolefin  compound,based on polyolefin resin,is produced and pelletized by special technology with adding special modifier,flame retardant,anti-oxidant and other special additivers.
3.Processing Technology
The  compound  can  be  processed  with  conventional  extruders,and  the  screw  with  a  mininum  20:1  L/D  and  a compression ratio of 1.2 is recommended.
The following temperature profile of extruder is recommended:
Type	Extruder body 1		Extruder body 2	Extruder body 3	Extruder body 4		Extruder body 5	Extruder head	Die head
T-PO001	135		145	155	165		160	155	155
Note:Compound should be dried at 70~80°C before use,which storage time has exceeded 2 months.
4.Packaging Storage and transport: Packaging:25kg/bag,Aluminim  foli  and  PE  mambrane  inside  bag  and  Kraft  outside  bag.
Storage and transport: Avoiding in direct sunlight and weathering.The storage place should be in clean ,cool ,dry and ventilated conditions.

5.Properties
No.	Inspected Properties		Unit	Standard Requirement	Inspection Result
1	Density		g/cm	1.35-1.55	1.52
2	Tensile Strength		MPa	≥10	11
3	Elongation at Break		%	≥150	175
4	Thermal Aging100±2°ºC×240 h Tensile Strength rate of change		%	≤±30	+9.6
	Elongation at Break rate of change		%	≤±30	-11.7
5	Thermal deformation90ºC×4h		%	≤50	12
6	Impact embrittlement temperature(-40ºC)			-40ºC	Pass
				≤15/30
7	Oxygen index		%	≥30	33
8	Acidity of gases evolved(PH value)		/	≥4.3	5.5
9	Conductivityof gases evolved		μs/mm	≤10	1.2
10	Content of halogen			≤5	1.1
11	Volume Resistivity at 20ºC		Ω.m	≥1.0×10¹	6.10×10
12	Toxicity Index			≤5	1.1
13	Cracking-resistan			Condition 6mm-150ºC-2kg-1h No cracking	Pass
14	Dielectric strength		MV/m	≥18	22
15	Hardness		HA	≥80	95
Note:Typical values are representative values in actual tests for reference only.

What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products