| Customization: | Available |
|---|---|
| Application: | Communication |
| Type: | as Customized |
|
Still deciding? Get samples of US$ 50/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Reference Standard TUV 2PFG1169 Typical Physical And Mechanical Properties Are As Follows: | ||||||||||||||||||||||||||||
| Item | Unit | Test Method | Typical | |||||||||||||||||||||||||
| Density | g/cm3 | GB/T1033.1 | 1.46 | |||||||||||||||||||||||||
| Tensile Strength | Mpa | GB/T1040.3-2006 | 13.2 | |||||||||||||||||||||||||
| Elongation At Break | % | GB/T1040.3-2006 | 165 | |||||||||||||||||||||||||
| Low Temperature Impact Embrittlement Temperature (-40 ºC) | … | GB/T 5470-2008 | Pass | |||||||||||||||||||||||||
| Volume Resistivity (20 ºC) | Ω·m | GB/T1410-2006 | 1.7×1012 | |||||||||||||||||||||||||
| Smoke Density 25 kW/m2 | Without Flames | GB/T8323.2-2008 | 245 | |||||||||||||||||||||||||
| With Flames | -- | GB/T8323.2-2008 | 45 | |||||||||||||||||||||||||
| Oxygen Index | % | GB/T2406.2-2009 | 34 | |||||||||||||||||||||||||
| Thermal Aging Performance 158ºC*168h |
Tensile Strength | Mpa | GB/T 32129-2015 | 14.4 | ||||||||||||||||||||||||
| Maximum Change Rate Of Tensile Strength | % | 9 | ||||||||||||||||||||||||||
| Elongation At Break | % | 140 | ||||||||||||||||||||||||||
| Maximum Change Rate Of Elongation At Break | % | -15,2 | ||||||||||||||||||||||||||
| Thermal Extension 200ºC*15min*0.2MPa |
Elongation Under Load | % | GB/T 2951.21-2008 | 45 | ||||||||||||||||||||||||
| Maximum Permanent Deformation After Cooling | % | 0 | ||||||||||||||||||||||||||
| Dielectric Strength | MV/m | GB/T1408.1-2006 | 22 | |||||||||||||||||||||||||
| Acidity of Gas Released by Combustion | HCl & HBr | % | GB/T17650.1-1998 | 0 | ||||||||||||||||||||||||
| HF | % | IEC 60684-2:2003 | 0 | |||||||||||||||||||||||||
| PH | -- | GB/T17650.2-1998 | 5.5 | |||||||||||||||||||||||||
| Conductivity | μS/mm | GB/T17650.2-1998 | 7.5 | |||||||||||||||||||||||||
| *Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data. |
||||||||||||||||||||||||||||