Photovoltaic Cable Sheathing Material Irradiation Crosslinking Flame Retardant Po/Poe Polyolefin LSZH Compound

• Customization: Available
• CAS No.: 9002-88-4
• Formula: (Cnh2)N
• Model NO.: T-PO013
• Usage: General Plastics, Engineering Plastics, Specialty Plastics, for Photovoltaic Cable Material
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Origin: China
• Package Size: 60.00cm * 95.00cm * 10.00cm
• Package Gross Weight: 25.000kg

Product Description

T-PO013 Series Irradiation Crosslinking Low Smoke Halogen-Free Flame Retardant PO/POE Compound Polyolefin For Photovoltaic Cable Material
Suitable For Electrical Installation Cable Of Indoor And Outdoor Solar Energy Equipment, Meeting The Requirements Of Tuv 2PFG 1169 Standard.
 

Reference Standard TUV 2PFG1169 Typical Physical And Mechanical Properties Are As Follows:

Item

Unit

Test Method

Typical

Density

g/cm^3

GB/T1033.1

1.46

Tensile Strength

Mpa

GB/T1040.3-2006

13.2

Elongation At Break

%

GB/T1040.3-2006

165

Low Temperature Impact Embrittlement Temperature (-40 ºC)

…

GB/T 5470-2008

Pass

Volume Resistivity (20 ºC)

Ω·m

GB/T1410-2006

1.7×10^12

Smoke Density 25 kW/m^2

Without Flames

GB/T8323.2-2008

245

With Flames

--

GB/T8323.2-2008

45

Oxygen Index

%

GB/T2406.2-2009

34

Thermal Aging Performance 158ºC*168h

Tensile Strength

Mpa

GB/T 32129-2015

14.4

Maximum Change Rate Of Tensile Strength

%

9

Elongation At Break

%

140

Maximum Change Rate Of Elongation At Break

%

-15,2

Thermal Extension 200ºC*15min*0.2MPa

Elongation Under Load

%

GB/T 2951.21-2008

45

Maximum Permanent Deformation After Cooling

%

0

Dielectric Strength

MV/m

GB/T1408.1-2006

22

Acidity of Gas Released by Combustion

HCl & HBr

%

GB/T17650.1-1998

0

HF

%

IEC 60684-2:2003

0

PH

--

GB/T17650.2-1998

5.5

Conductivity

μS/mm

GB/T17650.2-1998

7.5

*Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data.

 Packaging Storage And Transport
The material must be supplied packaged in such a way as to be protected during transport, handling and storage. The packaging must be in plastic bags, "bigbag", or cardboard box. The packaging must have adequate strength and be free of impurities that may contaminate the product and be protected against moisture as well.

What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products