90º C Flame Retardant -60º C Cold-Resistant PVC Plastic Environmental Friendly Compound Polyvinyl Chloride Sheathing Granules PVC

• Customization: Available
• CAS No.: 9002-86-2
• Formula: C2h3cl
• Model NO.: T-PV001
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: White Black with Color Masterbatch If Needed
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Origin: China

Product Description

Description

Based on pvc resin,Environmental Friendly pvc plastic is a granular material made by mixing, plasticizing, and granulating with plasticizers, flame retardants, stabilizers, and cold resistant additives. PVC plastic has good dielectric properties and is widely used in the insulation layer of wires and cables, as well as in the manufacture of electrical equipment.

Feature

Environmental friendly polyvinyl chloride has good insulation;
PVC plastic has weather resistance;
Chemical corrosion resistance;
Plasticity and flexibility;

Application

Insulation and jacketing materials for fiber optic cables;
Widely used in pvc pipes, window profiles, films, sheets, tubes, shoes, fittings;

FAQ

1.What Kind of Company are We?
Shanghai Gengyun Industrial Co., Ltd., based on the development of technology forum OF telecom optical&electric cable equipment and materials(TOEM), is mainly engaged in investment, trade, and technical services in the field of telecom optical & electric cable.
We provide our customers with complete materials demand solutions, as well as overall solutions and customized services in factory design, equipment configuration, product development and raw material supply.
2.Is our product single?
We have quite a wide variety of products.
Our products contain raw materials for optical fiber & cable, telecommunication cable include PE, PVC, FRP, PBT, water blocking yarn, water blocking tape, optical fiber ink, optical fiber, steel plastic composite tape, aluminum plastic composite tape, aramid yarn, etc. and
equipment for cable manufacturing including high-speed fiber coloring and rewinding machine, fiber merging machine, fiber screening and rewinding machine, special fiber drawing machine, coating production line, high-speed cable forming production line. There are different models of products under each category, and customization is supported.
3.Are Samples Available?
For most raw materials and optical cables, we can provide samples, but you need to bear the shipping costs; for cable manufacturing equipment, we can provide factory test reports of various indicators
4.Why Choose Our Company?
Our company was established in 2008 and has 16 years of experience in the communications industry. We can provide professional optoelectronic cable solutions and support product customization. Our products and raw materials are 100% in line with industry standards. We have warehouses all over the country, such as Shanghai, Jiangsu, Qingdao, Beijing and so on.

Type
This product has good physical and mechanical properties, low-temperature performance, and extrusion processing performance, and is suitable for wire and cable sheath materials with heat resistance temperature of 90 ºC and requirements for cold resistance and flame retardancy.
Performance

Properties		Units	Detection Method	Typical Value
Density		g/cm^3	GB/T 1033.1	1.23
Tensile strength		MPa	GB/T 1040.3	15.4
Elongation at break		%	GB/T 1040.3	456
After ageing in air oven		MPa	GB/T 8815	14.7
100±2ºC×240h
Tensile strength
Maximum variation for tensile strength		%		-5
Elongation at break		%		414
Maximum variation for elongation at break		%		-9
Mass loss		g/m2		36.6
Hot deformation 121ºC×1h		%	GB/T 8815	58
Stabilization time at 200ºC		min	GB/T 8815	105
Low temperature brittleness test		ºC	GB/T 5470	Pass
Oxygen index ( A )		--	GB/T 2406.2	26
Volume resistivity at 20ºC		Ω•m	GB/T 8815	2.1×10^10
Break down voltage		MV/m	GB/T 1408.1	22

Extrusion process
The product can be used with a regular PVC extruder, with a screw length to diameter ratio of L/D ≥ 20 Taking machine φ 90 as an example, it is recommended to place two layers of filter screens with 40 mesh/80 mesh on the mesh plate, with the best extrusion surface being smooth and the cross-section having no pores.
The product refering to the extrusion processing temperature:

Postion

Barrel Zone1

Barrel Zone 2

Barrel Zone 3

Barrel Zone 4

Head and Mold

Temperature(ºC)

170±10

180±10

190±10

195±10

190±10

*This process is based on our existing knowledge and experience, but due to the customer's usage conditions not within our control, the above recommended process is only for reference. It is recommended that users choose appropriate materials and production processes based on their extrusion equipment and cable structure. The above parameters are not applicable for quality control indicators.

Packaging Storage And Transport
25kg per bag, using aluminum plastic composite double bag.
Cable materials should not be exposed to sunlight or rain during transportation and should be stored in a clean, cool, dry, and ventilated warehouse.


What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Product