Environmental Friendly High-Quality Recycled XLPE MDPE Black Granules Cross-Linked Polyethylene PE Sheath Material

• Customization: Available
• CAS No.: 9002-88-4
• Formula: (C2h4) N
• Model NO.: T-PE001
• Material: Polyethylene/PE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics, Cross-Linked Flame Retardant Wires and Cables
• Plastic Properties After Heated: Thermoplastic Plastics
• Color: White Black with Color Masterbatch If Needed
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Origin: China

Product Description

T-PE001 Black Medium density environmental friendly recycled polyethylene sheath material is made of high-density polyethylene resin and linear low-density polyethylene resin as the main base material, antioxidant, lubricant and other additives,blending modification and granulation. The product has excellent mechanical properties and weather resistance and is suitable for optical cable and cable outer sheath.
Colour: White,Black(With Color Masterbatch If You Need Other Colour)
Processing Technology
The general extruder is used for processing, and the BM screw with length diameter ratio of more than 25 is selected. It is recommended to dry the material before use. The drying time is 1 hour and the temperature is 70 ~ 90 ºC , Extruder temperature setting, take model 90 as an example.

zone		Zone 1		Zone 2		Zone 3		Zone 4		Zone 5		Zone 6		Neck	Die
Temperature(ºC)		180		200		210		220		230		230		230	230

Test items

Unit

Typical value

Test Method

Melt flow Index(190ºC/2.16kg)

g/10min

~ 0.7 0.9

GB/T 3682

Density

g/cm3

0.946

GB/T 1033.1

Tensile Strength at Break

MPa

29

GB/T 1040.3

Elongation at Break

%

950

GB/T 1040.3

110ºC×240h Aging test

Tensile Strength at Break after aging

MPa

28

GB/T 1040.3

Fracture tensile strain after aging

%

900

GB/T 1040.3

Content of Carbon black

%

~ 2.45 2.75

GB/T 2951.41

Carbon black dispersion

Level

≤3

GB/T 18251

Oxidation induction period at 200ºC

min

>50

GB/T 2951.42

Low temperature impact(-76ºC)

≤15/30

PASS

GB/T 5470

ESCR(50ºC , 10% Igepal)

F0/h

>1000

GB/T 2951.41

Dielectric Strength

MV/m

30

GB/T 1408.1

Dielectric Constant

/

2.45

GB/T 1409

20ºC Volume Resistivity

Ω.m

2.0×10^14

GB/T 1410

Note: Typical values are representative values in actual tests and cannot be used as criteria for judgment.
Packaging:25kg per package, polyethylene inner bag, kraft paper composite bag and outer bag.
750 kg per pack, polyethylene inner bag and polypropylene ton outer bag
Transportation And Storage: store in a clean, dry, cool and ventilated warehouse on pallets ; During
transportation, it shall be protected from sun, rain, water immersion and scratch
Shelf life of materials: Six months from the date of production. If the shelf life is exceeded, the drying time shall be extended to 2 hours.       
                                 
What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products