Environmental Friendly LDPE plastic raw material is polyolefin crosslinking semi-conductive shielding cable sheath material, using high-quality EVA resin, conductive carbon black as the main materials, adding cross-linking agent, antioxidant and other additives,mixed and granulated. The process is stable and the quality is reliable. The product is used for 10kV crosslinking polyethylene insulated cable conductor and insulation layer crosslinking semi-conductive shielding material.
1. Good flexibility and weather resistance;
2. Good processing performance and formability;
3. Environmental Friendly LDPE Plastic has good chemical stability;
4. LDPE plastic raw material has high flame retardant;
5. Excellent environmental protection;
6. High oil resistance;
Low Density Recycled Polyethylene LDPE is mainly used to make cable insulation sheaths;
It can also be used for film products, such as agricultural films and packaging films;
It can also be used for various injection molding products. Such as containers, bottle caps, etc.
1.What Kind of Company are We?
Shanghai Gengyun Industrial Co., Ltd., based on the development of technology forum OF telecom optical&electric cable equipment and materials(TOEM), is mainly engaged in investment, trade, and technical services in the field of telecom optical & electric cable.
We provide our customers with complete materials demand solutions, as well as overall solutions and customized services in factory design, equipment configuration, product development and raw material supply.
2.Is our product single?
We have quite a wide variety of products.
Our products contain raw materials for optical fiber & cable, telecommunication cable include PE, PVC, FRP, PBT, water blocking yarn, water blocking tape, optical fiber ink, optical fiber, steel plastic composite tape, aluminum plastic composite tape, aramid yarn, etc. and
equipment for cable manufacturing including high-speed fiber coloring and rewinding machine, fiber merging machine, fiber screening and rewinding machine, special fiber drawing machine, coating production line, high-speed cable forming production line. There are different models of products under each category, and customization is supported
3.Are samples available?
For most raw materials and optical cables, we can provide samples, but you need to bear the shipping costs; for cable manufacturing equipment, we can provide factory test reports of various indicators
4.Why Choose Our Company?
Our company was established in 2008 and has 16 years of experience in the communications industry. We can provide professional optoelectronic cable solutions and support product customization. Our products and raw materials are 100% in line with industry standards. We have warehouses all over the country, such as Shanghai, Jiangsu, Qingdao, Beijing and so on.
Package
In 25kg PP woven bag, or per your requirement.
20mt/20'FCL
LDPE Injection Grade
Tests |
Value |
Unit |
Melt Flow Rate (MFR) |
15 |
g/10min |
Density |
0.922 |
g/cm3 |
Tensile Yield Strength |
7 |
Mpa |
Elongation at Break |
75 |
% |
Wien Softening Point |
85 |
°C |
LDPE Film Grade
Tests |
Value |
Unit |
Melt Flow Rate (MFR) |
2 |
g/10min |
Density |
0.9225 |
g/cm3 |
Tensile Strength |
9 |
Mpa |
Elongation at Break |
500 |
% |
Fish eye max(0.3-2mm) |
30 |
n/1200cm2 |
Stripes |
20 |
cm/20m3 |
T-PE004 Series PE/LDPE/LLDPE/MDPE/HDPE Raw Materials For Sheath Of Optical Fiber Cable
New Materials For Outer Sheath of High-Voltage Power&Rf&Outdoor Optical Cables, etc
Reference Standard GB/T15065-2009 Typical Physical And Mechanical Properties Are As Follows: |
Item |
|
Unit |
Test Method |
Typical |
Density |
|
g/cm3 |
GGB/T 1033.1 |
0.965 |
Melt Flow Rate |
|
g/10min |
GB/T 3682-2000 |
0.39 |
Tensile Strength |
|
Mpa |
GB/T1040.3-2006 |
26 |
Elongation At Break |
|
% |
GB/T1040.3-2006 |
830 |
Low Temperature Impact Embrittlement Temperature (-76 ºC) |
|
* |
GB/T 5470-2008 |
Pass |
Volume Resistivity (20 ºC) |
|
|
GB/T1410-2006 |
1.6×1014 |
Thermal Aging Performance 110ºC*240h |
Rate Of Change Of Tensile Strength |
% |
GB/T 2951.12-2008 |
9.6 |
Rate Of Change Of Breaking Tensile |
% |
12.1 |
Environmental Stress Crack Resistance |
|
Fo/h |
GB/T2951.41-2008 |
Pass |
Dielectric Strength |
|
MV/m |
GB/T1408.1-2006 |
26.8 |
200ºC OIT |
|
min |
GB/T2951.42-2008 |
53 |
Dielectric Constant |
|
|
GB/T1409-2006 |
2.62 |
Dielectric Loss Factor |
|
|
GB/T1409-2006 |
0.004 |
Carbon Black Content |
|
|
GB/T2951.41-2008 |
2.66 |
Vicat Softening Point |
|
ºC |
GB/T1633-2000 |
112 |
*Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS.
Note: The above typical values are random sampling data. |
Packaging Storage And Transport
The material must be supplied packaged in such a way as to be protected during transport, handling and storage. The packaging must be in plastic bags, "bigbag", or cardboard box. The packaging must have adequate strength and be free of impurities that may contaminate the product and be protected against moisture as well.
What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products