LDPE is polyolefin crosslinking semi-conductive shielding cable sheath material, using high-quality EVA resin, conductive carbon black as the main materials, adding cross-linking agent, antioxidant and other additives,mixed and granulated. The process is stable and the quality is reliable. The product is used for 10kV crosslinking polyethylene insulated cable conductor and insulation layer crosslinking semi-conductive shielding material.
Good flexibility and weather resistance;
Good processing performance and formability;
LDPE Injection Grade
Tests | Value | Unit |
Melt Flow Rate (MFR) | 15 | g/10min |
Density | 0.922 | g/cm3 |
Tensile Yield Strength | 7 | Mpa |
Elongation at Break | 75 | % |
Wien Softening Point | 85 | °C |
Tests | Value | Unit |
Melt Flow Rate (MFR) | 2 | g/10min |
Density | 0.9225 | g/cm3 |
Tensile Strength | 9 | Mpa |
Elongation at Break | 500 | % |
Fish eye max(0.3-2mm) | 30 | n/1200cm2 |
Stripes | 20 | cm/20m3 |
Reference Standard GB/T15065-2009 Typical Physical And Mechanical Properties Are As Follows: | ||||||||||||||||||||||||||||
Item | Unit | Test Method | Typical | |||||||||||||||||||||||||
Density | g/cm3 | GGB/T 1033.1 | 0.965 | |||||||||||||||||||||||||
Melt Flow Rate | g/10min | GB/T 3682-2000 | 0.39 | |||||||||||||||||||||||||
Tensile Strength | Mpa | GB/T1040.3-2006 | 26 | |||||||||||||||||||||||||
Elongation At Break | % | GB/T1040.3-2006 | 830 | |||||||||||||||||||||||||
Low Temperature Impact Embrittlement Temperature (-76 ºC) | * | GB/T 5470-2008 | Pass | |||||||||||||||||||||||||
Volume Resistivity (20 ºC) | GB/T1410-2006 | 1.6×1014 | ||||||||||||||||||||||||||
Thermal Aging Performance 110ºC*240h | Rate Of Change Of Tensile Strength | % | GB/T 2951.12-2008 | 9.6 | ||||||||||||||||||||||||
Rate Of Change Of Breaking Tensile | % | 12.1 | ||||||||||||||||||||||||||
Environmental Stress Crack Resistance | Fo/h | GB/T2951.41-2008 | Pass | |||||||||||||||||||||||||
Dielectric Strength | MV/m | GB/T1408.1-2006 | 26.8 | |||||||||||||||||||||||||
200ºC OIT | min | GB/T2951.42-2008 | 53 | |||||||||||||||||||||||||
Dielectric Constant | GB/T1409-2006 | 2.62 | ||||||||||||||||||||||||||
Dielectric Loss Factor | GB/T1409-2006 | 0.004 | ||||||||||||||||||||||||||
Carbon Black Content | GB/T2951.41-2008 | 2.66 | ||||||||||||||||||||||||||
Vicat Softening Point | ºC | GB/T1633-2000 | 112 | |||||||||||||||||||||||||
*Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data. |