| Application: | Communication, FTTH Network |
|---|---|
| Type: | Single-mode Fiber |
| Connection Structure: | Customized |
| Material Shape: | Round Wire |
| Allowed Lateral Pressure: | 100(N/100mm) |
| Allowed Tensile Strength: | <100N |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Characteristics Conditions Units Specified Values |
| Optical Characteristics |
| Attenuation |
| 1310nm dB/km ≤0.35 |
| 1550nm dB/km ≤0.22 |
| 1625nm dB/km ≤0.24 |
| 1383nm dB/km ≤0.32 |
| Attenuation vs. Wavelength |
| 1310nm 1285-1330nm dB/km ≤0.04 |
| 1550nm 1525-1575nm dB/km ≤0.02 |
| 1550nm 1480-1580nm dB/km ≤0.05 |
| Dispersion coefficients |
| 1288-1339nm ps/(nm·km) ≥-3.5,≤3.5 |
| 1371-1360nm ps/(nm·km) ≥-5.3,≤5.3 |
| 1480-1580nm ps/(nm·km) ≤20 |
| 1550nm ps/(nm·km) ≤18 |
| 1625nm ps/(nm·km) ≤22 |
| Zero dispersion wavelength nm 1302-1322 |
| Zero dispersion slope ps/(nm2·km) ≤0.090 |
| Zero dispersion slope typical value ps/(nm2·km) 0.086 |
| PMD: |
| Maximum Individual Fiber ps/√¯km 0.2 |
| Link Design Value(M=20,Q=0.01%) ps/√¯km 0.1 |
| Typical Value ps/√¯km 0.04 |
| Cable cutoff wavelengthλcc nm ≤1260 |
| Fiber cutoff wavelengthλc nm 1180-1330 |
| Mode field diameter(MFD) 1310nm μm 8.7±0.4 |
| 1550nm μm 9.6±0.5 |
| Effective group index of refraction |
| 1310nm 1.4672 |
| 1550nm 1.4683 |
| Attenuation Discontinuity 1310nm dB/km ≤0.05 |
| 1550nm dB/km ≤0.05 |
| Attenuation Bidirectional Measurement |
| 1310nm dB/km ≤0.05 |
| 1550nm dB/km ≤0.05 |
| Attenuation Uniformity 1310nm dB/km ≤0.05 |
| 1550nm dB/km ≤0.05 |
| Welding Loss |
| Average Value 1310nm,1550nm dB ≤0.05 |
| Maximum Value 1310nm,1550nm dB ≤0.1 |
| Geometrical Characteristics |
| Cladding diameter μm 125±0.7 |
| Cladding non-circularity % ≤0.8 |
| Core-cladding concentricity error μm ≤0.5 |
| Coating diameter μm 245±5 |
| Cladding-coating concentricity μm ≤12 |
| Coating non-circularity % ≤3.0 |
| Curl m ≥4 |
| Environmental Characteristics (1310nm,1550nm,1625nm) |
| Temperature Dependence -60ºC ~+85ºC dB/km ≤0.05 |
| Damp heat dependence 85ºC,RH85%,30days dB/km ≤0.05 |
| Water Immersion 23ºC,30days dB/km ≤0.05 |
| Heat Aging 85ºC,30days dB/km ≤0.05 |
| Mechanical Specification |
| Proof test % ≥1.02 |
| N ≥9.0 |
| Gpa ≥7.04 |
| Coating strip force Peak force N 1.3-8.9 |
| Typical average force N 1.9 |
| Tensile Strength Weibull Probability 50% Mpa ≥4000 |
| Weibull Probability 15% Mpa ≥3050 |
| Dynamic stress corrosion susceptibility parameter Nd ≥27 |
| Macro-bend Loss |
| 10 turn around a mandrel of 15mm radius |
| 1550nm dB ≤0.03 |
| 1625nm dB ≤0.1 |
| 1 turn around a mandrel of 10mm radius |
| 1550nm dB ≤0.1 |
| 1625nm dB ≤0.2 |
| 1 turn around a mandrel of 7.5mm radius |
| 1550nm dB ≤0.4 |
| 1625nm dB ≤0.8 |