| Customization: | Available |
|---|---|
| Molecular Principal Chain: | Element Organic Polymer |
| Color: | Customized |
|
Still deciding? Get samples of US$ 50/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Low volatile content, less condensation on cooling tubes | |||||||||||||||
| Suitable for wet-on-dry drawing processes | |||||||||||||||
| Higher viscosity, faster drawing speed, good for non-helium drawing condition | |||||||||||||||
| Combining with RT series primary coating and inks for even better results |
| No. | Properties | Units | Standards | |||||||||||
| Before Curing (Liquid) | ||||||||||||||
| 1 | Viscosity,25ºC | mPa.s | 7800-8600 | |||||||||||
| 2 | Density,20ºC | g/cm3 | 1.12-1.13 | |||||||||||
| 3 | Solid Content | % | >99 | |||||||||||
| 4 | Refractive Index,25ºC | 1.51±0.005 | ||||||||||||
| After Curing (Solid) | ||||||||||||||
| 5 | Glass Transition Temperature (DMA) |
ºC | ≥50 | |||||||||||
| 6 | Secant Modules,2.5% | MPa | 700-850 | |||||||||||
| 7 | Elongation | % | 12-28 | |||||||||||
| 8 | Tensile Strength | MPa | 30-40 | |||||||||||
| 9 | Cure speed when RAU95% | J/cm2 | ≥0.50 | |||||||||||
| 10 | Oxygen generation(80ºC , 24h) | ul/g | ≤0.2 | |||||||||||
| 11 | Weight Change | 88ºC 8weeks | % | <-1.0 | ||||||||||
| 125ºC 8weeks | <-4.6 | |||||||||||||
| 12 | (15g/m2 on PE) Coefficient of Friction |
>0.20 | ||||||||||||
| * 75μ m film was made by curing under the nitrogen condition at UVA 0.5J/cm2 with a Fusion D lamp,unless otherwise specified. UV Dosemeter is by UV POWER PUCK®II from EIT.INC.USA. |
||||||||||||||