| Reference Standard JB/T10491-2004Typical Physical And Mechanical Properties Are As Follows: | ||||||||||||||||||||||||||||
| Item | Unit | Test Method | Typical | |||||||||||||||||||||||||
| Density | g/cm3 | GB/T1033.1 | 1.48 | |||||||||||||||||||||||||
| Tensile Strength | Mpa | GB/T1040.3-2006 | 11.5 | |||||||||||||||||||||||||
| Elongation At Break | % | GB/T1040.3-2006 | 175 | |||||||||||||||||||||||||
| Low Temperature Impact Embrittlement Temperature (-40 ºC) | … | GB/T 5470-2008 | Pass | |||||||||||||||||||||||||
| Volume Resistivity (20 ºC) | Ω·m | GB/T1410-2006 | 1.8×1012 | |||||||||||||||||||||||||
| Smoke Density 25 kW/m2 | Without Flames | … | GB/T8323.2-2008 | 245 | ||||||||||||||||||||||||
| With Flames | … | GB/T8323.2-2008 | 45 | |||||||||||||||||||||||||
| Oxygen Index | % | GB/T2406.2-2009 | 32 | |||||||||||||||||||||||||
| Thermal Aging Performance 135ºC*168h |
Tensile Strength | Mpa | GB/T 32129-2015 | 12.5 | ||||||||||||||||||||||||
| Maximum Change Rate Of Tensile Strength | % | 8.7 | ||||||||||||||||||||||||||
| Elongation At Break | % | 158 | ||||||||||||||||||||||||||
| Maximum Change Rate Of Elongation At Break | % | -9.7 | ||||||||||||||||||||||||||
| Thermal Extension 200ºC*15min*0.2MPa |
Elongation Under Load | % | GB/T 2951.21-2008 | 50 | ||||||||||||||||||||||||
| Maximum Permanent Deformation After Cooling | % | 0 | ||||||||||||||||||||||||||
| Dielectric Strength | MV/m | GB/T1408.1-2006 | 25 | |||||||||||||||||||||||||
| Acidity of Gas Released by Combustion | HCl & HBr | % | GB/T17650.1-1998 | 0 | ||||||||||||||||||||||||
| HF | % | EC 60684-2:2003 | 0 | |||||||||||||||||||||||||
| PH | … | GB/T17650.2-1998 | 5.5 | |||||||||||||||||||||||||
| Conductivity | μS/mm | GB/T17650.2-1998 | 7.5 | |||||||||||||||||||||||||
| *Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data. |
||||||||||||||||||||||||||||
1.What Kind of Company Are We?
Shanghai Gengyun Industrial Co., Ltd., based on the development of technology forum OF telecom optical&electric cable equipment and materials(TOEM), is mainly engaged in investment, trade, and technical services in the field of telecom optical & electric cable.
We provide our customers with complete materials demand solutions, as well as overall solutions and customized services in factory design, equipment configuration, product development and raw material supply.
2.Why Choose Our Company?
Our company was established in 2008 and has 16 years of experience in the communications industry. We can provide professional optoelectronic cable solutions and support product customization. Our products and raw materials are 100% in line with industry standards. We have warehouses all over the country. Such as Shanghai, Jiangsu, Qingdao, Beijing and so on.
3.Are Samples Free?
For most raw materials,optical fiber and optical cables, we can provide free samples. For cable manufacturing equipment, we can provide factory test reports of various indicators.
4.Is the Product Variety Rich?
We have quite a wide variety of products.
Our products contain raw materials for optical fiber & cable, telecommunication cable include PE, PVC, FRP, PBT, water blocking yarn, water blocking tape, optical fiber ink, optical fiber, steel plastic composite tape, aluminum plastic composite tape, aramid yarn, etc. and
equipment for cable manufacturing including high-speed fiber coloring and rewinding machine, fiber merging machine, fiber screening and rewinding machine, special fiber drawing machine, coating production line, high-speed cable forming production line. There are different models of products under each category, and customization is supported.
What We Have In The Field Of Telecom Optical & Electric Cable :
){kind=link}