Still deciding? Get samples of $ !
Order Sample
|
| Customization: | Available |
|---|---|
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Reference Standard TUV 2PFG 1169 Typical Physical And Mechanical Properties Are As Follows: | ||||||||||||||||||||||||||||
| Item | Unit | Test Method | Typical | |||||||||||||||||||||||||
| Density | g/cm3 | GB/T1033.1 | 1.48 | |||||||||||||||||||||||||
| Tensile Strength | Mpa | GB/T 1040.3-2006 | 11.0 | |||||||||||||||||||||||||
| Elongation At Break | % | GB/T 1040.3-2006 | 180 | |||||||||||||||||||||||||
| Low Temperature Impact Embrittlement Temperature (-40 ºC) | … | GB/T 5470-2008 | Pass | |||||||||||||||||||||||||
| Volume Resistivity (20 ºC) | Ω·m | GB/T 1410-2006 | 1.8×1012 | |||||||||||||||||||||||||
| Smoke Density 25kW/m2 | Without Flames | … | GB/T 8323.2-2008 | 245 | ||||||||||||||||||||||||
| With Flames | … | GB/T 8323.2-2008 | 45 | |||||||||||||||||||||||||
| Oxygen Index | % | GB/T 2406.2-2009 | 32 | |||||||||||||||||||||||||
| Thermal Aging Performance 135ºC*168h |
Tensile Strength | Mpa | GB/T 32129-2015 | 11.8 | ||||||||||||||||||||||||
| Maximum Change Rate Of Tensile Strength | % | 7.3 | ||||||||||||||||||||||||||
| Elongation At Break | % | 165 | ||||||||||||||||||||||||||
| Maximum Change Rate Of Elongation At Break | % | -8.3 | ||||||||||||||||||||||||||
| Thermal Extension 200ºC*15min*0.2MPa |
Elongation Under Load | % | GB/T 2951.21-2008 | 40 | ||||||||||||||||||||||||
| Maximum Permanent Deformation After Cooling | % | 0 | ||||||||||||||||||||||||||
| Dielectric Strength | MV/m | GB/T 1408,.1-2006 | 25 | |||||||||||||||||||||||||
| Acidity of Gas Released by Combustion | HCl & HBr | % | GB/T 17650.1-1998 | 0 | ||||||||||||||||||||||||
| HF | % | IEC 60684-2:2003 | 0 | |||||||||||||||||||||||||
| PH | … | GB/T 17650.2-1998 | 5.5 | |||||||||||||||||||||||||
| Conductivity | μS/mm | GB/T17650.2-1998 | 7.5 | |||||||||||||||||||||||||
| *Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data. |
||||||||||||||||||||||||||||