| Low modulus,high elongation value | |||||||||||||||
| Suitable for both Hg lamps and LED lamps curing | |||||||||||||||
| Stable Viscosity -Temperature property, easy for process | |||||||||||||||
| Low curing energy requirements, easy to be stripped | |||||||||||||||
| Low COF value, smooth coating surface |
| No. | Properties | Units | Standards | |||||||||||
| Before Curing (Liquid) | ||||||||||||||
| 1 | Viscosity,25ºC | mPa.s | 3000-3500 | |||||||||||
| 2 | Density,20ºC | g/cm3 | 1.11-1.12 | |||||||||||
| 3 | Refractive Index,25ºC | 1.49±0.005 | ||||||||||||
| 4 | Solid Content | % | >99 | |||||||||||
| After Curing (Solid) | ||||||||||||||
| 5 | Secant Modules,2.5% | MPa | 150-250 | |||||||||||
| 6 | Elongation | % | >35 | |||||||||||
| 7 | Tensile Strength | MPa | 10-26 | |||||||||||
| 8 | *Cure speed when RAU% ≥ 95% | J/cm2 | ≥0.5 | |||||||||||
| * Refers to the curing state where the relative curing degree of liquid colored ink with a certain ink film thickness is ≥ 95% when exposed to ultraviolet light |
||||||||||||||