CAS No.: | 9002-88-4 |
---|---|
Formula: | (C2h4)N |
Material: | Polyethylene/PE |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Extrusion |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Type | Product | Application | |||||||||
T-SM003G-0808 | Optical cable used framework material | Used for the slotted core cable |
Zone | Zone1 | Zone2 | Zone3 | Zone4 | Zone5 | Head | Die | ||||
ºC Temperature |
165 | 165 | 170 | 170 | 170 | 170 | 170 | ||||
NO. | ltem | Unit | Typical value | Test method |
1 | Melting Index | g/10min | 0.3 | GB/T2951.41 |
2 | Density | g/cm3 | 0.952 | GB1033 |
3 | Tensile Strength | MPa | 28 | GB1040 |
4 | Yield strength | MPa | 26 | GB1040 |
5 | Elongation at Break | % | 800 | GB1040 |
6 | Low temperature elongation at break | % | 487 | GB/T2951.13 |
7 | (-76ºC) Brittle temperature |
pc | 0/10 | GB5470 |
8 | ESCR | h | >1000 | GB/T2951.39 |
9 | 200ºC OIT |
Min | 45 | GB/T2951.37 |
10 | Dielectric Strength | KV/m | 28 | GB1408 |
11 | Volume Resistivity at 20ºC | Ω ·m | 4.5×1014 | GB1410 |
12 | Dielectric constant | 2.1 | GB1409 | |
13 | Dielectric loss tangent | 0.0003 | GB1409 |