| Customization: | Available |
|---|---|
| Application: | Communication |
| Type: | as Customized |
|
Still deciding? Get samples of US$ 50/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Reference Standard YD/T1113-2015 Typical Physical And Mechanical Properties Are As Follows: | ||||||||||||||||||||||||||||
| Item | Unit | Test Method | Typical | |||||||||||||||||||||||||
| Density | g/cm3 | GB/T 1033.1 | 1.45 | |||||||||||||||||||||||||
| Tensile Strength | Mpa | GB/T1040.3-2006 | 12.7 | |||||||||||||||||||||||||
| Elongation At Break | % | GB/T 1040.3-2006 | 188 | |||||||||||||||||||||||||
| Low Temperature Impact Embrittlement Temperature (-40 ºC) | … | GB/T 5470-2008 | Pass | |||||||||||||||||||||||||
| Volume Resistivity (20 ºC) | Ω.m | GB/T 1410-2006 | 1.8×1010 | |||||||||||||||||||||||||
| Smoke Density 25 Kw/m ² | Without Flames | … | GB/T8323.2-2008 | 225 | ||||||||||||||||||||||||
| With Flames | … | GB/T 8323.2-2008 | 40 | |||||||||||||||||||||||||
| Oxygen Index | % | GB/T 2406.2-2009 | 33 | |||||||||||||||||||||||||
| Thermal aging performance: 100ºC*168h |
Tensile Strength | Mpa | GB/T 2951.12-2008 | 11.3 | ||||||||||||||||||||||||
| Maximum Change Rate Of Tensile Strength | % | -11 | ||||||||||||||||||||||||||
| Elongation At Break | % | 158 | ||||||||||||||||||||||||||
| Maximum Change Rate Of Elongation At Break | % | -16 | ||||||||||||||||||||||||||
| Thermal Deformation(90ºC,9.8N) | % | GB/T 8815-2008 | 10 | |||||||||||||||||||||||||
| Brinell Hardness HA | … | GB/T 2411 | 90 | |||||||||||||||||||||||||
| Heat Resistant Stress Cracking | … | GB/T15065-2009 | Uncracked | |||||||||||||||||||||||||
| Resistance To Environmental Stress Cracking | Fo/h | GB/T 2951,41-2008 | Pass | |||||||||||||||||||||||||
| Acidity Of Gas Released By Combustion | HCI & HBr | % | GB/T17650.1-1998 | 0 | ||||||||||||||||||||||||
| HF | % | IEC 60684-2:2003 | 0 | |||||||||||||||||||||||||
| PH | GB/T17650.2-1998 | 5.5 | ||||||||||||||||||||||||||
| Conductivity | μS/mm | GB/T 17650.2-1998 | 7.5 | |||||||||||||||||||||||||
| *Appearance: Uniform color and no impurities. Evaluation: Qualified, meeting the requirements specified by ROHS. Note: The above typical values are random sampling data. |
||||||||||||||||||||||||||||