Low Shrink High Density Polyethylene PE Compound

• Customization: Available
• CAS No.: 9002-88-4
• Formula: (C2h4)N
• Model NO.: T-SM004
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Black
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Trademark: TOEM
• Origin: China
• Package Size: 1.10cm * 1.10cm * 1.10cm
• Package Gross Weight: 1300.000kg

Product Description

T-SM004 Series
T-SM004H0802-HLS adopts import polyethylene resin as raw material.It has features of high size stability,smooth surface,low shrinkage performance,processing and mechanical properties.

Type and Application

Type			Product					Application
T-SM004H0802-HLS			Low shrink high density polyethylene cable material					Used for manufacturing of Blowing Tiny Cables

Processing
The following temperature profile of extruder is recommended:

Zone				Zone1	Zone2	Zone3	Zone4		Zone5	Head	Die
ºC Temperature				200	220	230	240		245	240	240

Properties

No.	Item	Unit	Typical value	Test method
1	Melting Index	g/10min	0.27	GB/T2951.41
2	Density	g/cm^3	0.951	GB1033
3	Tensile Strength	MPa	33	GB1040
4	Yield strength	MPa	20	GB1040
5	Elongation at Break	%	810	GB1040
6	Low temperature elongation at break	%	480	GB/T2951.13
7	(-76ºC) Brittle temperature	pc	0/10	GB5470
8	ESCR	h	>1000	GB/T2951.39
9	200ºC OIT	Min	60	GB/T2951.37
10	Dielectric Strength	KV/m	28	GB1408
11	Volume Resistivity at 20ºC	Ω ·m	4.5×10^14	GB1410
12	Dielectric constant		2.1	GB1409
13	Dielectric loss tangent		0.0003	GB1409
14	Cabling shrinkage	%	0.04
15	Surface roughness			GB/T 1031-1995
	Ra	μm	0.49
	Ry	μm	3.2

Storage and Transport    
It is hygroscopic.It should be stored in dry and ventilated warehouse.And drying treatment is required after long-term storage.Drying temperature is 75ºC.Drying time is 3 hours,and storage period should be less than 12 months.

                 
What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Product