LSZH Low Smoke Zero Halogen Flame Retardant Virgin Recycled Polyolefin Poe/PE Compound Sheath Material

• CAS No.: 9002-88-4
• Formula: (Cnh2)N
• Material: Polyolefin
• Usage: General Plastics, Engineering Plastics, Specialty Plastics, FTTH Drop Cable
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Model NO.: T-PO005
• Color: White Black with Color Masterbatch If Needed
• Transport Package: Bag/Pallet
• Specification: 25kg/bag
• Origin: China

Product Description

Thermoplastic Low-Smoke Zero-Halogen Flame Retardant Compound Polyolefin
Product Description
Thermoplastic low-smoke zero-halogen and flame retardant polyolefin compound, based on polyolefin resin, is produced and pelletized by special technology with adding special modifier, flame retardant, anti-oxidant and other special additivers.
Colour: White,Black(With Color Masterbatch If You Need Other Colour)
Type And Application

Type			Product    Name				Application
T-PO005			Thermoplastic  low-smoke  zero-halogen  and  flame  retardant  polyolefin  compounds				Compliance with ROHS ,applicable to covered wire cable

Processing Technology
The compound can be processed with conventional extruders, and the screw with a mininum 20:1 L/D and a compression ratio of 1.2 is recommended.
The following temperature profile of extruder is recommended:

Type		Extruder body 1		Extruder body 2	Extruder body 3	Extruder body 4		Extruder body 5	Extruder head		Die head
T-PO005		135		145	155	165		160	155		155

Note: Compound should be dried at 70~80ºC before use, which storage time has exceeded 2 months.

Packaging Storage And Transport
Packaging:25kg/bag,Aluminim foli and PE mambrane inside bag and Kraft outside bag.
Storage and transport :Avoiding in direct sunlight and weathering. The storage place should be in clean,cool,dry and ventilated conditions.
Properties

No.	Inspected properties						Unit	Standard requirement		Inspection result
1	Density						g/cm^3	1.3-- 1.4		1.33
2	Tensile Strength						MPa	≥10		15
3	Elongation at Break						%	≥ 300		415
4	Thermal Aging100±2ºC×240 h						%	≤ ±20		+7.5
	Tensile Strength rate of change
	Elongation at Break rate of change						%	≤ ±20		-9.2
5	Thermal deformation90ºC×4h						%	≤20		4
6	Impact embrittlement temperature(-40ºC)						--	-40ºC		Pass
								≤15/30
7	Moisture						%	≤0. 12		0. 1
8	Oxidation Induction Time						min	≥30		60
9	Volume Resistivity at 20ºC						Ω .m	≥1.0 × 1012		8.40× 1013
10	Dielectric strength						MV/m	≥18		23
11	Oxygen index						%	≥22		24
12	Hardness						HA	≥80		94

Note:Typical values are representative values in actual tests for reference only.



What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Products