| Customization: | Available |
|---|---|
| Molecular Principal Chain: | Element Organic Polymer |
| Color: | Customized |
|
Still deciding? Get samples of US$ 50/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Faster curing speed | |||||||||||||||
| Low volatile content, less condensation on cooling tubes | |||||||||||||||
| Excellent process properties, higher viscosity, can be used for non-Helium drawing | |||||||||||||||
| Suitable for both wet-on-wet and wet-on-dry processes |
| No. | Properties | Units | Standards | |||||||||||
| Before Curing (Liquid) | ||||||||||||||
| 1 | Viscosity,25ºC | mPa.s | 8000-8600 | |||||||||||
| 2 | Density,20ºC | g/cm3 | 1.02-1.03 | |||||||||||
| 3 | Solid Content | % | >99 | |||||||||||
| 4 | Refractive Index,25ºC | 1.47±0.005 | ||||||||||||
| After Curing (Solid) | ||||||||||||||
| 5 | Glass Transition Temperature (DMA) |
ºC | ≤-30 | |||||||||||
| 6 | Secant Modules,2.5% | MPa | 1.1-1.4 | |||||||||||
| 7 | Elongation | % | 90-180 | |||||||||||
| 8 | Tensile Strength | MPa | 0.8-1.4 | |||||||||||
| 9 | Cure speed when RAU95% | J/cm2 | ≥0.30 | |||||||||||
| 10 | Oxygen generation(80ºC , 24h) | ul/g | ≤0.2 | |||||||||||
| 11 | Weight Change | 88ºC 8weeks | % | <-3.8 | ||||||||||
| 125ºC 8weeks | <-7.5 | |||||||||||||
| 12 | Adhesion on glass |
50% RH | N | >0.45 | ||||||||||
| 95% RH | >0.35 | |||||||||||||
| * 75μ m film was made by curing under the nitrogen condition at UVA 0.5J/cm2 with a Fusion D lamp,unless otherwise specified. UV Dosemeter is by UV POWER PUCK II from EIT.INC.USA. |
||||||||||||||