| Properties | |||||
| No. | Inspected Properties | Unit | Standard Requirement |
Inspection Result | |
| 1 | Density | g/cm | 1.35-1.55 | 1.52 | |
| 2 | Tensile Strength | MPa | ≥10 | 11 | |
| 3 | Elongation at Break | % | ≥150 | 175 | |
| 4 | Thermal Aging100±2°ºC×240 h Tensile Strength rate of change |
% | ≤±30 | +9.6 | |
| Elongation at Break rate of change | % | ≤±30 | -11.7 | ||
| 5 | Thermal deformation90ºC×4h | % | ≤50 | 12 | |
| 6 | Impact embrittlement temperature(-40ºC) | -40ºC | Pass | ||
| ≤15/30 | |||||
| 7 | Oxygen index | % | ≥30 | 33 | |
| 8 | Acidity of gases evolved(PH value) | / | ≥4.3 | 5.5 | |
| 9 | Conductivityof gases evolved | μs/mm | ≤10 | 1.2 | |
| 10 | Content of halogen | ≤5 | 1.1 | ||
| 11 | Volume Resistivity at 20ºC | Ω.m | ≥1.0×10¹ | 6.10×10 | |
| 12 | Toxicity Index | ≤5 | 1.1 | ||
| 13 | Cracking-resistan | Condition 6mm-150ºC-2kg-1h No cracking |
Pass | ||
| 14 | Dielectric strength | MV/m | ≥18 | 22 | |
| 15 | Hardness | HA | ≥80 | 95 | |
| Note:Typical values are representative values in actual tests for reference only. | |||||